is dedicated to perpetuating the noble art of blacksmithing. A blacksmith is one who shapes and forges iron with hammer and anvil. ABANA encourages and facilitates the training of blacksmiths; disseminates information about sources of material and equipment; exposes the art of blacksmithing to the public; serves as a center of information about blacksmithing for the general public, architects, interior designers, and other interested parties.

ABANA 2018 Conference

WhyABANA?
Why ABANA Contest
Social Media
Contest

Tempil Chart






1/ TRANSFORMATION RANGE In this range steels undergo internal atomic changes which radically affect the properties of  the material.
2/
LOWER TRANSFORMATION TEMPERATURE (A1). Termed Ac1 on heating, Ar1 on cooling. Below Ac1 structure ordinarily consists of FERRITE and PEARLITE (see below). On heating through Ac1 these constituents begin to dissolve in each other to form AUSTENITE (see below) which is nonmagnetic. This dissolving action continues on heating through the TRANSFORMATION RANGE until the solid solution is complete at the upper transformation temperature.
3/
UPPER TRANSFORMATION TEMPERATURE (A3). Termed Act on heating Ar3 on cooling. Above this temperature the structure consists wholly of AUSTENITE which coarsens with increasing time and temperature. Upper transformation temperature is lowered as carbon increases to 0.85% (eutectoid point).

FERRITE is practically pure iron (in plain carbon steels) existing below the lower transformation temperature. It is magnetic and has very slight solid solubility for carbon.

PEARLITE is a mechanical mixture of FERRITE and CEMENTITE.

CEMENTITE or IRON CARBIDE is a compound of iron and carbon, Fe3C.

AUSTENITE is the non magnetic form of iron and has the power to dissolve carbon and alloying elements.
4/
ANNEALING frequently referred to as FULL ANNEALING consists of heating steels to slightly above Ac3 holding for AUSTENITE to form, then slowly cooling in order to produce small grain size softness good ductility and other desirable properties. On cooling slowly the AUSTENITE transforms to FERRITE and PEARLITE.
5/
NORMALIZING consists of heating steels to slightly above Ac3 holding for AUSTENITE to form, then followed by cooling (in still air). On cooling, AUSTENITE transforms giving somewhat higher strength and hard ness and slightly less ductility than in annealing.
6/
FORGING RANGE extends to several hundred degrees above the UPPER TRANSFORMATION TEMPERATURE.
7/
BURNING RANGE is above the FORGING RANGE. Burned steel is ruined and cannot be cured except by remelting.
8/
STRESS RELIEVING consists of heating to a point below the LOWER TRANSFORMATION TEMPERATURE holding for a sufficiently long period to relieve locked-up stresses, then slowly cooling. This process is sometimes called process annealing.
9/
BLUE BRITTLE RANGE occurs approximately from 300° to 700°F. Peening or working of steels should not be done between these temperatures, since they are more brittle in this range than above or below it.
10/
PREHEATING FOR WELDING is carried out to prevent crack formation. See TEMPIL° PREHEATING CHART for recommended temperature for various steels and non-ferrous metals.
11/
CARBURIZING consists of dissolving carbon into surface of steel by heating to above transformation range in presence of carburizing compounds.
12/
NITRIDING consists of heating certain special steels to about 1000°F for long periods in the presence of ammonia gas. Nitrogen is absorbed into the surface to produce extremely hard "skins".
13/
SPHEROIDIZING consists of heating to just below the lower transformation temperature, A1, for a sufficient length of time to put the CEMENTITE constituent of PEARLITE into globular form. This produces softness and in many cases good machinability. MARTENSITE is the hardest of the transformation products of AUSTENITE and is formed only on cooling below a certain temperature known as the M3 temperature (about 400° to 600°F for carbon steels). Cooling to this temperature must be sufficiently rapid to prevent AUSTENITE from transforming to softer constituents at higher temperatures.   

EUTECTOID STEEL contains approximately 0.85% carbon.   

FLAKING occurs in many alloy steels and is a defect characterized by localized micro-cracking and "cake like" fracturing. It is usually attrib uted to hydrogen bursts. Cure consists of cycle cooling to at least 600°F before air-cooling.  

OPEN OR RIMMING STEEL has not been completely deoxidized and the ingot solidifies with a sound surface ("rim") and a core portion containing blowholes which are welded in subsequent hot rolling.   

KILLED STEEL has been deoxidized at least sufficiently to solidify without appreciable gas evolution.   

SEMI-KILLED STEEL has been partially deoxidized to reduce solidification shrinkage in the ingot.   

A SIMPLE RULE Brinell Hardness divided by two, times 1000, equals approximate Tensile Strength in pounds per square inch. (200 Brinell /2 X 1000 = approx. 100,000 Tensile Strength, p.s.i.).   

Tempilstiks are the easiest way for a blacksmith to determine high temperatures.